Concrete Aluminium Powder

Characteristic

conc- 75

Volatile matter % (max) (1)

0. 5

Metallic aluminium content (min) (2)

91

Density gm/cc (3)

0. 17-0. 20

Average particle size (typical) cilas 920

30µ

Sieve analysis (4)

Retained on 180µ

2% (max)

Passing through 45µ

65-75%

Gas reactivity test with ca(oh)2 for 0. 07 gn of aluminium powder at 25 degree c(5)

70-75ml of gas evolution within 16 minutes

Water miscibility test

100%

Packing

1. 440 mm dia 740 mm height with 7" dia mouth, inner lid and outer capseals.
2. 205 liters capacity m. S barrels.

Testing procedure

(1) (2) & (3) - is : 438 - 2006
(4) astm b 212 - 99
(5) & (6) in house testing procedure

Characteristic

Conc-40

Volatile Matter % (max) (1)

0.5

Metallic Aluminium Content (min) (2)

90

Density gm/cc (3)

0.18-0.22

Average Particle Size (Typical) Cilas 920

50µ

SIEVE ANALYSIS (4)

Retained on 180µ

3% (max)

Passing through 45µ

30-50%

Gas Reactivity test with Ca(OH)2 for 0.07 GN of Aluminium Powder at 25 degree C(5)

70-75ml of gas evolution within 16 minutes

Water Miscibility Test

100%

Packing

1. 440 mm Dia 740 mm Height with 7" Dia Mouth, inner Lid and outer capseals.
2. 205 Liters Capacity M.S Barrels.

Testing Procedure

(1) (2) & (3) - IS : 438 - 2006
(4) ASTM B 212 - 99
(5) & (6) In house testing procedure

Characteristic

Conc-95

Volatile Matter % (max) (1)

0.5

Metallic Aluminium Content (min) (2)

90

Density gm/cc (3)

0.18-0.25

Average Particle Size (Typical) Cilas 920

20µ

SIEVE ANALYSIS (4)

Retained on 180µ

1% (max)

Passing through 45µ

> 88%

Gas Reactivity test with Ca(OH)2 for 0.07 GN of Aluminium Powder at 25 degree C(5)

65ml(min) of gas evolution within 16 minutes

Water Miscibility Test

100%

Packing

1. 440 mm Dia 740 mm Height with 7" Dia Mouth, inner Lid and outer capseals.
2. 205 Liters Capacity M.S Barrels.

Testing Procedure

(1) (2) & (3) - IS : 438 - 2006
(4) ASTM B 212 - 99
(5) & (6) In house testing procedure